等静压力及偏置电压下锆钛锡酸铅基反铁电体的介电行为

戴中华; 姚熹; 徐卓

您当前的位置：

首页 >

文章列表页 >

等静压力及偏置电压下锆钛锡酸铅基反铁电体的介电行为

专题研究 | 更新时间：2025-12-08

- 等静压力及偏置电压下锆钛锡酸铅基反铁电体的介电行为
- Dielectric Behavior of Antiferroelectric Lead Lanthanum Zirconate Titanate Stannate Ceramics under Bias Voltage and Hydrostatic Pressure
- 西安交通大学学报 2007年41卷第2期页码：228-231+244
- 作者机构：
  
  西安交通大学电子材料与器件研究所,西安,710049
- 作者简介：
- 基金信息：
  
  : 2006-06-07. 作者简介: 戴中华(1970～),男,博士生;姚熹(联系人),男,教授,博士生导师,中国科学院院士. 基金项目: 国家重点基础研究发展规划资助项目(2002CB613307);国家自然科学基金资助项目(10474077)
- DOI：
  中图分类号： TQ174.6
- 网络首发：2007-02-10，
  
  纸质出版：2007
- 稿件说明：
移动端阅览
戴中华, 姚熹, 徐卓. 等静压力及偏置电压下锆钛锡酸铅基反铁电体的介电行为[J]. 西安交通大学学报, 2007,41(2):228-231+244.

戴中华, 姚熹, 徐卓. Dielectric Behavior of Antiferroelectric Lead Lanthanum Zirconate Titanate Stannate Ceramics under Bias Voltage and Hydrostatic Pressure[J]. 2007, 41(2): 228-231+244.
戴中华, 姚熹, 徐卓. 等静压力及偏置电压下锆钛锡酸铅基反铁电体的介电行为[J]. 西安交通大学学报, 2007,41(2):228-231+244. DOI：

戴中华, 姚熹, 徐卓. Dielectric Behavior of Antiferroelectric Lead Lanthanum Zirconate Titanate Stannate Ceramics under Bias Voltage and Hydrostatic Pressure[J]. 2007, 41(2): 228-231+244. DOI：

摘要

采用固态烧结工艺制备了位于反铁电(AFE)/铁电(FE)相界附近的PbLa(Zr

Ti)O

(PLZST)反铁电陶瓷样品.通过测定样品的相对介电常数及损耗与各种参量的关系

得到了等静压力及偏置电压对反铁电体铁电/反铁电相变及反铁电/顺电(PE)相变温度影响的规律.研究发现:极化了的PLZST反铁电材料在一定等静压力的作用下

随着偏置电压的增加其峰值相对介电常数增大

相对介电常数最大值对应的温度降低

FE/AFE转变温度上升

AFE/PE转变温度下降; 当等静压力为0.1 MPa时

单位偏置电压引起的居里点变化率为-1 ℃/kV

单位偏置电压引起的FE/AFE相变温度变化率为5.2 ℃/kV

当等静压力为60 MPa时

分别为-2.2 ℃/kV和3 ℃/kV.

Abstract

Antiferroelectric PbLa(Zr

Ti)O

(PLZST)ceramics sample near the ferroelectric(FE)-antiferroelectric(AFE)phase boundary are prepared by a traditional solid-state reaction process. The influences of the bias voltage and hydrostatic pressure on FE/AFE and AFE/PE phase transition and transition temperature of these PLZST ceramics obtained by measuring the relation between the relative dielectric constants and loss and various parameters of samples. It is found that under certain hydrostatic pressure

the dielectric constants of polarized antiferroelectric PLZST increase

and the temperature corresponding to the maximum of relative dielectric constants decreases with in

creasing bias voltage. At the same time

the FE/AFE transition temperature increases and AFE/PE transition temperature decreases. Under the hydrostatic pressure of 0.1 MPa

the change rate of Curie temperature caused by unit bias voltage of this ceramics is -1 ℃/kV and the change rate of FE/AFE transition temperature caused by unit bias voltage is 5.2 ℃/kV; under the pressure of 60 MPa

are -2.2 ℃/kV and 3 ℃/kV respectively.

关键词

Keywords

references

Pan W Y, Pan C Q, Zhang Q M, et al. Principles and applications of ferroelectrics and related materials [M]. Oxford: Clarendon Press, 1977:221.

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

离子液体改性燃料的电流体动力学效应研究

面向高海拔空冷发电机防晕性能演化规律的电热耦合研究

混合电解槽阵列协同的风光耦合制氢系统双层多目标优化

结构-语义-残差协同的图像压缩框架：面向隐私保护与高保真重建

语义区分和子图整合驱动的知识图谱表示学习方法