用NH<sub>4</sub>Cl-H<sub>2</sub>O溶液共晶凝固实验模拟Bridgman法晶体生长过程

李恒; 白博峰; 苏燕兵; 张磊; 郭烈锦

您当前的位置：

首页 >

文章列表页 >

用NH₄Cl-H₂O溶液共晶凝固实验模拟Bridgman法晶体生长过程

专题研究 | 更新时间：2025-12-08

- 用NH₄Cl-H₂O溶液共晶凝固实验模拟Bridgman法晶体生长过程
- Experimental Investigation of NH₄Cl-H₂O Eutectic Solution Solidification for Simulating Crystal Growth with Bridgman Method
- 西安交通大学学报 2007年41卷第11期页码：1298-1302
- 作者机构：
  
  西安交通大学动力工程多相流国家重点实验室,西安,710049
- 作者简介：
- 基金信息：
  
  : 2007-04-09. 作者简介: 李恒(1980～),男,博士生;白博峰(联系人),男,副教授. 基金项目: 国家自然科学基金资助项目(50536040);教育部新世纪优秀人才支持计划资助项目(NCET-04-0923)
- DOI：
  中图分类号： TK12
- 网络首发：2007-11-10，
  
  纸质出版：2007
- 稿件说明：
移动端阅览
李恒, 白博峰, 苏燕兵, 等. 用NH₄Cl-H₂O溶液共晶凝固实验模拟Bridgman法晶体生长过程[J]. 西安交通大学学报, 2007,41(11):1298-1302.

李恒, 白博峰, 苏燕兵, et al. Experimental Investigation of NH₄Cl-H₂O Eutectic Solution Solidification for Simulating Crystal Growth with Bridgman Method[J]. 2007, 41(11): 1298-1302.
李恒, 白博峰, 苏燕兵, 等. 用NH₄Cl-H₂O溶液共晶凝固实验模拟Bridgman法晶体生长过程[J]. 西安交通大学学报, 2007,41(11):1298-1302. DOI：

李恒, 白博峰, 苏燕兵, et al. Experimental Investigation of NH₄Cl-H₂O Eutectic Solution Solidification for Simulating Crystal Growth with Bridgman Method[J]. 2007, 41(11): 1298-1302. DOI：

摘要

利用NH

Cl-H

O溶液的共晶凝固模拟Bridgman法晶体生长过程

通过粒子图像测速系统测量了矩形腔和圆柱腔内NH

Cl-H

O溶液共晶凝固过程中的流场

结合温度变化得到了凝固过程中流动和温度的耦合规律.实验结果表明:在侧壁和底部冷却条件下

两种腔室内溶液共晶凝固过程中流场的变化基本相似

形成竖壁面附近溶液向下流动、中心区域溶液向上流动的对流涡; 凝固开始后

热交换和潜热的释放使液相区内温度下降趋于平缓; 圆柱腔内出现了角区绕流和二次对流涡现象.实验得到的流动和温度变化规律为理论建模及数值计算提供了有用的实验数据.

Abstract

The crystal growth process with Bridgman method was simulated via NH

Cl-H

O solution eutectic solidification. The flow fields of NH

Cl-H

O solution during solidification in both rectangular cavity and cylindrical cavity were measured with particle image velocimetry(PIV). With the temperature varying

the coupling rules of fluid flow and temperature during eutectic solidification process were observed. Cooling both at sidewall and bottom

the evolution of flow field was about the same in the two kinds of cavities during the solidification process. Convection vortex occurred in the liquid region flowing downward along the vertical sidewalls

and upward in the center region. Heat transfer and latent heat release made the temperature decrease slowly. The rule between flow field and temperature during the eutectic solidification approached the crystal growth process of Bridgman method

and offered valuable data for theoretical modeling and numerical calculation.

关键词

Keywords

references

Kaneko K, Koyaguchi T. Solidification of an aqueous ammonium chloride solution in rectangular cavity, I: experimental study [J]. Int Journal of Heat and Mass Transfer, 1989, 32(1): 47-68.

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

透平叶栅二次流瞬态特性的新测试方法

采用试验设计方法的第三代CO2气体箔轴承箔片几何参数敏感性分析

融合物理信息与深度算子网络的变压器绕组热-流场快速计算方法

混合电解槽阵列协同的风光耦合制氢系统双层多目标优化

多工况下离心压气机叶轮-机匣一体联合设计优化

用NH4Cl-H2O溶液共晶凝固实验模拟Bridgman法晶体生长过程

Experimental Investigation of NH4Cl-H2O Eutectic Solution Solidification for Simulating Crystal Growth with Bridgman Method

DOI：

摘要

Abstract

关键词

Keywords

references

用NH₄Cl-H₂O溶液共晶凝固实验模拟Bridgman法晶体生长过程

Experimental Investigation of NH₄Cl-H₂O Eutectic Solution Solidification for Simulating Crystal Growth with Bridgman Method