Effect of Pre-Oxidation on Corrosion Behavior of Typical Heat-Resistant Materials in High Temperature CO<sub>2</sub>

XU Yiming; LIU Shijie; WANG Shuo; LIANG Zhiyuan; ZHAO Qinxin

doi:10.7652/xjtuxb202205011

您当前的位置：

首页 >

文章列表页 >

Effect of Pre-Oxidation on Corrosion Behavior of Typical Heat-Resistant Materials in High Temperature CO₂

更新时间：2025-07-09

- Effect of Pre-Oxidation on Corrosion Behavior of Typical Heat-Resistant Materials in High Temperature CO₂
- Vol. 56, Issue 5, Pages: 105-118(2022)
- 作者机构：
  
  1. 西安交通大学热流科学与工程教育部重点实验室,西安,710049
  2. 哈尔滨锅炉厂有限责任公司,哈尔滨,150046
- 作者简介：
- 基金信息：
- DOI：10.7652/xjtuxb202205011
  CLC： TL341
- Online First：10 May 2022，
  
  Published：2022
- 稿件说明：
移动端阅览
XU Yiming, LIU Shijie, WANG Shuo, et al. Effect of Pre-Oxidation on Corrosion Behavior of Typical Heat-Resistant Materials in High Temperature CO₂[J]. 2022, 56(5): 105-118. DOI: 10.7652/xjtuxb202205011.
DOI：

XU Yiming, LIU Shijie, WANG Shuo, et al. Effect of Pre-Oxidation on Corrosion Behavior of Typical Heat-Resistant Materials in High Temperature CO₂[J]. 2022, 56(5): 105-118. DOI: 10.7652/xjtuxb202205011. DOI：

摘要

为提高耐热材料在高温CO

中的抗腐蚀性能

以耐热材料Sanicro 25、HR6W、HR230和740H为对象

经高温O

短时预氧化后开展CO

腐蚀实验。采用分析天平测量耐热材料腐蚀前后质量变化; 利用X射线衍射仪、扫描电镜及能谱分析仪表征腐蚀产物形貌、成分及其分布。实验结果表明:预氧化后耐热材料在900 ℃ CO

中的腐蚀动力学曲线符合抛物线规律; 预氧化后4种耐热材料表面氧化物主要为Cr的氧化物和少量零星团状的Fe氧化物

该富Cr氧化膜有效减低腐蚀行为的离子扩散

从而降低耐热材料的腐蚀质量增加; 耐热材料Sanicro 25和HR6W表面腐蚀层厚度减薄

而740H内氧化加剧。结合耐热材料腐蚀质量变化与腐蚀产物

高温预氧化处理可提高HR6W和HR230的抗高温CO

腐蚀性能。

Abstract

To improve the corrosion resistance of heat-resistant materials in high-temperature CO

such heat-resistant materials as Sanicro 25

HR6W

HR230 and 740H are pre-oxidized for a short period in high-temperature O

and then tested for their corrosion resistance. An analytical balance is used to measure the mass of the heat-resistant materials before and after the test. X-ray diffractometer

scanning electron microscope and energy dispersive analyzer are used to characterize the morphology

composition and distribution of corrosion products. The test results show that the corrosion kinetics curves of the pre-oxidized heat-resistant materials in

900 ℃ CO

conform to the parabolic law; the surface oxides of the four heat-resistant materials after pre-oxidation are mainly Cr oxides and a small amount of sporadic Fe oxides

the Cr-rich oxide film effectively reduces the ion diffusion during the corrosion process

thereby reducing the corrosion weight gain of these materials. The corrosion layer on the surface of Sanicro 25 and HR6W is thinned

while the oxidation in 740H is intensified. It can be seen from their mass changes and corrosion products that high-temperature pre-oxidation can improve the corrosion resistance of HR6W and HR230 in high-temperature CO

关键词

Keywords

references

姚李超, 邹正平, 付超, 等. 超临界二氧化碳再压缩布雷顿循环性能分析及优化设计方法研究 [J]. 推进技术, 2022, 43(3): 85-94.

YAO Lichao, ZOU Zhengping, FU Chao, et al. Performance analysis of supercritical carbon dioxide recompression Brayton cycle and research on optimization design method [J]. Journal of Propulsion Technology, 2022, 43(3): 85-94.

童家麟, 赵寅丰. 超临界二氧化碳布雷顿循环研究进展 [J]. 精细与专用化学品, 2021, 29(1): 6-11.

TONG Jialin, ZHAO Yinfeng. The progress review of supercritical CO2 Brayton cycle research [J]. Fine and Specialty Chemicals, 2021, 29(1): 6-11.

董力. 超临界二氧化碳发电技术概述 [J]. 中国环保产业, 2017(5): 48-52.

DONG Li. Summarization on power technology of supercritical carbon dioxide [J]. China Environmental Protection Industry, 2017(5): 48-52.

邓成刚, 李伟科, 梁展鹏, 等. 太阳光热发电超临界二氧化碳循环系统经济性分析与优化 [J]. 热力发电, 2021, 50(5): 59-66.

DENG Chenggang, LI Weike, LIANG Zhanpeng, et al. Economic analysis and optimization for concentrated solar power-supercritical carbon dioxide Brayton cycle system [J]. Thermal Power Generation, 2021, 50(5): 59-66.

毛世杰, 杨英英, 武卫东, 等. S-CO2布雷顿循环系统中合金腐蚀行为研究进展 [J]. 中国电机工程学报, 2021, 41(8): 2782-2790.

MAO Shijie, YANG Yingying, WU Weidong, et al. Study of corrosion behavior of alloys in supercritical CO2 Brayton cycle power generation: a review [J]. Proceedings of the CSEE, 2021, 41(8): 2782-2790.

阳绪东, 潘绍成, 尹朝强, 等. 舰船动力系统中超临界CO2循环的应用分析 [J]. 技术与市场, 2020, 27(9): 1-3.

YANG Xudong, PAN Shaocheng, YIN Chaoqiang, et al. Supercritical carbon dioxide cycle and its application in shipboard power system [J]. Technology and Market, 2020, 27(9): 1-3.

杨竞择, 杨震, 段远源. 超临界二氧化碳布雷顿循环塔式光热系统及光伏光热混合系统运行性能分析 [J]. 热力发电, 2020, 49(10): 93-100.

YANG Jingze, YANG Zhen, DUAN Yuanyuan. Operational performance analysis of CSP and PV-CSP systems based on supercritical carbon dioxide Brayton cycle [J]. Thermal Power Generation, 2020, 49(10): 93-100.

徐进良, 刘超, 孙恩慧, 等. 超临界二氧化碳动力循环研究进展及展望 [J]. 热力发电, 2020, 49(10): 1-10.

XU Jinliang, LIU Chao, SUN Enhui, et al. Review and perspective of supercritical carbon dioxide power cycles [J]. Thermal Power Generation, 2020, 49(10): 1-10.

冯建闯. 超临界二氧化碳布雷顿循环发电系统热力学分析 [J]. 节能, 2019, 38(8): 34-38.

FENG Jianchuang. Thermodynamic analysis of supercritical carbon dioxide Brayton cycle power generation system [J]. Energy Conservation, 2019, 38(8): 34-38.

黄彦平, 王俊峰. 超临界二氧化碳在核反应堆系统中的应用 [J]. 核动力工程, 2012, 33(3): 21-27.

HUANG Yanping, WANG Junfeng. Applications of supercritical carbon dioxide in nuclear reactor system [J]. Nuclear Power Engineering, 2012, 33(3): 21-27.

秦志伟. 光热发电进入刚性需求阶段 [N]. 中国科学报, 2021-10-11(003).

桂雍, 梁志远, 郭亭山, 等. 超临界二氧化碳环境中耐热材料的腐蚀行为研究 [J]. 动力工程学报, 2021, 41(7): 602-608.

GUI Yong, LIANG Zhiyuan, GUO Tingshan, et al. Corrosion behavior of heat-resistant materials in supercritical carbon dioxide environment [J]. Chinese Journal of Power Engineering, 2021, 41(7): 602-608.

梁志远, 桂雍, 赵钦新. 超临界二氧化碳动力系统耐热材料高温腐蚀研究进展 [J]. 装备环境工程, 2020, 17(7): 88-93.

LIANG Zhiyuan, GUI Yong, ZHAO Qinxin. High temperature corrosion research progress of heat-resistant materials in supercritical carbon dioxide [J]. Equipment Environmental Engineering, 2020, 17(7): 88-93.

鲍颖群, 苟远波, 梁志远. 高效超超临界机组用材HR3C和HR6W的热腐蚀行为及机理研究 [J]. 材料保护, 2020, 53(7): 154-161.

BAO Yingqun, GOU Yuanbo, LIANG Zhiyuan. Hot corrosion behavior and mechanism of HR3C and HR6W used in advanced ultra-supercritical power plant [J]. Materials Protection, 2020, 53(7): 154-161.

李玉峰, 梁志远, 邓世丰, 等. 高温CO2环境下耐热合金HR6W和740H的腐蚀行为 [J]. 西安交通大学学报, 2020, 54(5): 179-188.

LI Yufeng, LIANG Zhiyuan, DENG Shifeng, et al. Corrosion behavior of heat resistant alloys HR6W and 740H in high-temperature carbon dioxide environment [J]. Journal of Xi'an Jiaotong University, 2020, 54(5): 179-188.

刘晓翠, 张转转, 刘锟, 等. Cu、Cr、Ni元素对高强耐候钢腐蚀稳定性的影响 [J]. 轧钢, 2019, 36(6): 17-21.

LIU Xiaocui, ZHANG Zhuanzhuan, LIU Kun, et al. Influence of copper, chromium and nickel on the corrosion resistance property of high strength weathering resistant steel [J]. Steel Rolling, 2019, 36(6): 17-21.

谢鑫, 赵义, 董广博, 等. Cr元素对工业环境用钢耐蚀性的影响 [J]. 电镀与精饰, 2021, 43(9): 13-18.

XIE Xin, ZHAO Yi, DONG Guangbo, et al. Influence of Cr on corrosion resistance of industrial environment steel [J]. Plating Finishing, 2021, 43(9): 13-18.

赵江涛, 任常飞, 张柳丽, 等. 元素Cr、Ni对不锈钢耐蚀性能影响 [J]. 现代机械, 2013(5): 88-91.

ZHAO Jiangtao, REN Changfei, ZHANG Liuli, et al. The influence of chromium and nickel on corrosion resistance of stainless steel [J]. Modern Machinery, 2013(5): 88-91.

LIANG Zhiyuan, YU Miao, GUI Yong, et al. Corrosion behavior of heat-resistant materials in high-temperature carbon dioxide environment [J]. JOM, 2018, 70(8): 1464-1470.

HOLCOMB G R, ALMAN D E. The effect of manganese additions on the reactive evaporation of chromium in NiCr alloys [J]. Scripta Materialia, 2006, 54(10): 1821-1825.

OLEKSAK R P, TYLCZAK J H, HOLCOMB G R, et al. Temperature-dependence of corrosion of Ni-based superalloys in hot CO2-rich gases containing SO2 impurities [J]. JOM, 2020, 72(5): 1822-1829.

ALLAN S J, DEAN M J. The effect of surface condition on the oxidation behavior of austenitic stainless steels in carbon dioxide and helium-based coolants [J]. In Behavior of High Temperature Alloys in Aggressive Environments, 1979, 6: 319-333.

HOLMES D R, HILL R B, WYATT L M. Corrosion of steels in CO2 [C]∥Proceedings of the British Nuclear Energy Society International Conference at Reading University. London, UK: The British Nuclear Energy Society, 1974: 23-24.

白银, 刘正东, 谢建新, 等. 预氧化处理对G115钢高温蒸气氧化行为的影响 [J]. 金属学报, 2018, 54(6): 895-904.

BAI Yin, LIU Zhengdong, XIE Jianxin, et al. Effect of pre-oxidation treatment on the behavior of high temperature oxidation in steam of G115 steel [J]. Acta Metallurgica Sinica, 2018, 54(6): 895-904.

OLEKSAK R P, ROUILLARD F. Materials performance in CO2 and supercritical CO2 [J]. Comprehensive Nuclear Materials(Second Edition), 2020, 4: 422-451.

OLEKSAK R P, HOLCOMB G R, CARNEY C S, et al. Effect of surface finish on high-temperature oxidation of steels in CO2, supercritical CO2, and air [J]. Oxidation of Metals, 2019, 92(5): 525-540.

JIANG He, DONG Jianxin, ZHANG Maicang, et al. Oxidation behavior and mechanism of Inconel 740H alloy for advanced ultra-supercritical power plants between 1050 and 1170 ℃ [J]. Oxidation of Metals, 2015, 84(1): 61-72.

于淼, 梁志远, 桂雍, 等. 4种先进超超临界电站锅炉用高温合金高温腐蚀性能实验研究 [J]. 表面技术, 2018, 47(6): 8-16.

YU Miao, LIANG Zhiyuan, GUI Yong, et al. Experimental study on high temperature resistance in simulated coal-ash environment of four superalloys for AUSC power plant boilers [J]. Surface Technology, 2018, 47(6): 8-16.

NGUYEN T D, ZHANG Jianqiang, YOUNG D J. Effects of Si, Al and Ti on corrosion of Ni-20Cr and Ni-30Cr alloys in Ar-20CO2 at 700 ℃ [J]. Corrosion Science, 2018, 130: 161-176.

NGUYEN T D, ZHANG Jianqiang, YOUNG D J, et al. Effects of Si, Al and Ti on corrosion of Ni-20Cr and Ni-30Cr alloys in Ar-20CO2-20H2O gas at 700 ℃ [J]. Corrosion Science, 2020, 170: 108702.

鲁金涛, 杨珍, 徐松乾, 等. Inconel 740H金在纯水蒸气环境中的高温氧化行为 [J]. 机械工程材料, 2015, 39(10): 37-41.

LU Jintao, YANG Zhen, XU Songqian, et al. High temperature oxidation behavior of Inconel alloy 740H in pure steam [J]. Materials for Mechanical Engineering, 2015, 39(10): 37-41.

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effects of Surface Scratches on Corrosion Behaviors of Heat-Resistant Steels T92,TP347H and TP347HFG in High-Temperature CO2

Research on High-Temperature Corrosion Behavior and Mechanisms of T91 Heat-Resistant Steel in Water-Cooled Walls of 630℃Ultra-Supercritical Power Generation Units

Research on High-Temperature Corrosion Behavior and Mechanisms of T91 Heat-Resistant Steel in Water-Cold Walls of 630 °C Ultra-Supercritical Power Generation Units

Corrosion Behavior of Heat Resistant Alloys HR6W and 740H in High-Temperature Carbon Dioxide Environment

Corrosion Behavior of 316L Steel in Pseudocritical Region of Supercritical Water

Related Author

郭亭山

梁志远

王鹏

赵钦新

ZHAO Qinxin

SHAO Huaishuang

WEI Pengkai

LIANG Zhiyuan

Related Institution

MOE Key Laboratory of Thermo-Fluid Science and Engineering Xi 'an Jiaotong University

Harbin Boiler Works Co., Ltd., Haerbin

Harbin Boiler Works Co., Ltd.

MOE Key Laboratory of Thermo-Fluid Science and Engineering, Xi’an Jiaotong University

State Key Laboratory of Multiphase Flow in Power Engineering, Xi'an Jiaotong University

⁰

Effect of Pre-Oxidation on Corrosion Behavior of Typical Heat-Resistant Materials in High Temperature CO2

DOI：10.7652/xjtuxb202205011

摘要

Abstract

关键词

Keywords

references

Effect of Pre-Oxidation on Corrosion Behavior of Typical Heat-Resistant Materials in High Temperature CO₂